Complete Set of CAMPUS® Data, ASTM Data, Biopolymer Database, Application Database, Tradename Database, Literature Database, Toolbox.

Material datasheets available free. Online registration at: www.materialdatacenter.com

Material Data Center is a leading international information system for the plastics industry. Material Data Center offers a comprehensive plastics database, calculation tools, CAE interfaces, a literature database and an application database. For more information about Material Data Center visit www.materialdatacenter.com.

This is the free Material Data Center Datasheet of NORYL GTX™ Resin GTX810 - Americas - (PPE+PA*)-GF10 - Saudi Basic Industries Corporation (SABIC)

Material Data Center offers the following functions for NORYL GTX™ Resin GTX810 - Americas:
unit conversion, PDF datasheet print, comparison with other plastics, snap fit calculation, beam deflection calculation, CAE Interfaces

Check here, which other Noryl GTX datasheets, application examples or technical articles are available in Material Data Center

Use the following short links to get directly to the properties of interest in this datasheet:
Caracteristicas de procesamiento y fisicas - Propiedades mecánicas - Propiedades térmicas - Otras propiedades - Recomendación para procesamiento Moldeo por inyección
Any use of this information falls under the rules of our disclaimer.
Texto del producto
NORYL GTX™ 810 resin is a 10% glass reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade has high stiffness (flexural modulus 3000 MPa), excellent chemical resistance, and high heat resistance. NORYL GTX GTX810 resin is an excellent candidate for a wide variety of applications including electrical and lighting components, security (CCTV) housings.

UL Yellow Card Link E121562-101009449
Caracteristicas de procesamiento y fisicasValorUnidadesMétodo de ensayo
ISO Data
Indice de fluidez volumétrico, MVR 11 cm³/10min ISO 1133
Temperatura 280 °C -
Carga 5 kg -
Contracción posterior al moldeo, paralelo 0.7 % ISO 294-4, 2577
Contracción posterior al moldeo, normal 1.0 % ISO 294-4, 2577
ASTM Data
Índice de fluidez, MFI 12 g/10min ASTM D 1238
Temperatura 280 °C -
Carga 5 kg -
Contracción posterior al moldeo, paralelo 0.66 mm/mm ASTM D 955
Contracción posterior al moldeo, normal 0.99 mm/mm ASTM D 955
Propiedades mecánicasValorUnidadesMétodo de ensayo
ISO Data
Módulo de tracción 4200 MPa ISO 527
Esfuerzo de fluencia 102 MPa ISO 527
Alarg. en límite elástico 3.9 % ISO 527
Resistencia a la tracción 95 MPa ISO 527
Alargamiento a rotura 5.2 % ISO 527
Modulo de Flexión 3900 MPa ISO 178
Resistencia al impacto Charpy, +23°C 60 kJ/m² ISO 179/1eU
Resistencia al impacto Charpy c/entalla, +23°C 6.5 kJ/m² ISO 179/1eA
Izod impact strength, +23°C, 4mm 85 kJ/m² ISO 180/1U
Res. impacto Izod c/entalla, +23°C, 4mm 6.8 kJ/m² ISO 180/1A
ASTM Data
Módulo de tracción 4050 MPa ASTM D 638
Esfuerzo de fluencia a tracción 96 MPa ASTM D 638
Esfuerzo de fractura a tracción 91 MPa ASTM D 638
Alargamiento a la fluencia 4 % ASTM D 638
Alargamiento a la rotura 5.5 % ASTM D 638
Módulo de flexión 3950 MPa ASTM D 790
Dureza Rockwell R 119 - ASTM D 785
Resistencia al impacto Izod con entalla, 1/8 in 80 J/m ASTM D 256
Resistencia al impacto Izod con entalla, baja temperatura 53 J/m ASTM D 256
Temperatura -30 °C -
Resistencia al impacto Izod, 1/8 in 740 J/m ASTM D 256
Propiedades térmicasValorUnidadesMétodo de ensayo
ISO Data
Estabilidad al calor, 1.80 MPa 192 °C ISO 75-1/-2
Estabilidad al calor, 0.45 MPa 241 °C ISO 75-1/-2
Temp. reblandecimiento Vicat, A 250 °C ISO 306
Temp. reblandecimiento Vicat, B 221 °C ISO 306
Coef.de expansión térmica lineal, paralelo 44 E-6/K ISO 11359-1/-2
Coef.de expansión térmica lineal, normal 87 E-6/K ISO 11359-1/-2
Combustibilidad a 1.5mm esp. nom. HB class IEC 60695-11-10
Espesores de probeta 1.5 mm -
ASTM Data
Estabilidad al calor @ 66 psi 239 °C ASTM D 648
Estabilidad al calor @ 264 psi 201 °C ASTM D 648
Temperatura Vicat 221 °C ASTM D 1525
Otras propiedadesValorUnidadesMétodo de ensayo
Absorción de agua 2.12 % Sim. to ISO 62
Densidad 1180 kg/m³ ISO 1183
Densidad 1160 kg/m³ ASTM D 792
Recomendación para procesamiento Moldeo por inyecciónValorUnidadesMétodo de ensayo
Temperatura de pre-secado 95 - 105 °C -
Tiempo de pre-secado 3 - 4 h -
Humedad de procesamiento ≤0.07 % -
Temperatura de la masa 280 - 305 °C -
Temperatura del molde 75 - 120 °C -
Zona 1 265 - 305 °C -
Zona 2 270 - 305 °C -
Zona 3 275 - 305 °C -
Velocidad de giro de husillo 20 - 100 rpm -
Contrapresión 0.3 - 1.4 MPa -
Características
Procesamiento y forma de entrega
Moldeo por inyección
Applicaciones
Automotriz
Disponibilidad regional
Norteamérica
Disclaimer
Copyright Altair Engineering GmbH. Altair Engineering GmbH assumes no liability for the system to be free of errors. The user takes sole responsibility for the use of this data under the exclusion of every liability from Altair Engineering GmbH; this is especially valid for claims of compensation resulting from consequential damages. Altair explicitly points out that any decision about the application of materials must be double checked with the producer of this material. This includes all contents of this system. Copyright laws are applicable for the content of this system.
Created: Source: www.materialdatacenter.com


Material Data Center is provided by M-Base Engineering + Software GmbH. M-Base Engineering + Software GmbH assumes no liability for the system to be free of errors. Any decision about the application of materials must be double checked with the producer of this material.

Additional information about this material, like producer contact address, etc. can be found at www.materialdatacenter.com. For access to this extra information a registration is requested. Free online registration is available.